Title: POLÍMEROS INORGÁNICOS ACTIVADOS ALCALINAMENTE. OBTENIDOS EMPLEANDO COMO MATERIAS PRIMAS ARCILLAS COMUNES DE BAILÉN
Authors: Fuentes-Ramírez, Antonio J.
metadata.dc.contributor.advisor: Pérez-Villarejo, Luis
Eliche-Quesada, Dolores
metadata.dc.contributor.other: Universidad de Jaén. Ingeniería Química, Ambiental y de los Materiales
Abstract: [ES]En este estudio, una arcilla illítica calcinada de Bailén (Jaén, España), arcilla amarilla (AA) se ha valorizado como reemplazo del metacaolín en la síntesis de nuevos materiales geopoliméricos. Las materias primas, arcilla cruda y caolín comercial, se pretrataron a 750 ° C (4 h). Varias muestras (0-100% en peso de arcilla) se activaron mezclando una solución de NaOH y una solución de silicato de sodio. Las muestras se curaron (60 ºC y 99% de humedad relativa) durante 24 h, luego se desmoldaron y se mantuvieron en condiciones ambientales durante 28 días. Los resultados indican que la incorporación de hasta un 50 % en peso de arcilla proporcionó a los geopolímeros una mayor resistencia mecánica (39,6 MPa), una mayor densidad aparente (1455 kg / m3), y una conductividad térmica similar, aunque ligeramente superior (0,25 W / mK) que los geopolímeros control que contienen solo metacaolín como precursor. [EN] In this study, a calcined illitic clay from Bailén (Jaén, Spain), was valorized as a substitute of metakaolin in the synthesis of new geopolymeric materials. The raw materials, raw clay and commercial kaolin, were pretreated at 750 °C (4 h). Several samples (0-100 wt. % of clay) were activated by mixing NaOH solution and sodium silicate solution. The specimens were cured (60 ºC and 99 % relative humidity) for 24 h, then demolded and kept at ambient conditions for 7, 28 and 90 days. The results indicated that the incorporation up to 50 wt % of raw clay provided geopolymers with higher mechanical strength (39.6 MPa) and bulk density (1455 kg/m3), and similar although slightly higher thermal conductivity (0.25 W/mK) than control geopolymers containing only metakaolin as precursor.
Issue Date: 15-Jul-2020